ジアクリル酸無水物
ジアクリル酸無水物 物理性質
- 融点 :
- -20 °C
- 沸点 :
- 85-86°C 17mm
- 比重(密度) :
- 1,094 g/cm3
- 闪点 :
- 77°C
- 貯蔵温度 :
- 2-8°C
- 溶解性:
- Chloroform (Sparingly), Ethyl Acetate (Slightly)
- 外見 :
- clear liquid
- 色:
- Colorless to Almost colorless
- 安定性::
- Moisture sensitive
- InChI:
- InChI=1S/C6H6O3/c1-3-5(7)9-6(8)4-2/h3-4H,1-2H2
- InChIKey:
- ARJOQCYCJMAIFR-UHFFFAOYSA-N
- SMILES:
- C(=O)(C=C)OC(=O)C=C
- CAS データベース:
- 2051-76-5(CAS DataBase Reference)
安全性情報
- リスクと安全性に関する声明
- 危険有害性情報のコード(GHS)
絵表示(GHS) |
|
注意喚起語 |
警告 |
危険有害性情報 |
コード |
危険有害性情報 |
危険有害性クラス |
区分 |
注意喚起語 |
シンボル |
P コード |
H302 |
飲み込むと有害 |
急性毒性、経口 |
4 |
警告 |
|
P264, P270, P301+P312, P330, P501 |
H315 |
皮膚刺激 |
皮膚腐食性/刺激性 |
2 |
警告 |
|
P264, P280, P302+P352, P321,P332+P313, P362 |
H317 |
アレルギー性皮膚反応を起こすおそれ |
感作性、皮膚 |
1 |
警告 |
|
P261, P272, P280, P302+P352,P333+P313, P321, P363, P501 |
H319 |
強い眼刺激 |
眼に対する重篤な損傷性/眼刺激 性 |
2A |
警告 |
|
P264, P280, P305+P351+P338,P337+P313P |
H335 |
呼吸器への刺激のおそれ |
特定標的臓器毒性、単回暴露; 気道刺激性 |
3 |
警告 |
|
|
|
注意書き |
P261 |
粉じん/煙/ガス/ミスト/蒸気/スプレーの吸入を避ける こと。 |
P264 |
取扱い後は皮膚をよく洗うこと。 |
P264 |
取扱い後は手や顔をよく洗うこと。 |
P280 |
保護手袋/保護衣/保護眼鏡/保護面を着用するこ と。 |
P301+P312 |
飲み込んだ場合:気分が悪い時は医師に連絡する こと。 |
P302+P352 |
皮膚に付着した場合:多量の水と石鹸で洗うこと。 |
P305+P351+P338 |
眼に入った場合:水で数分間注意深く洗うこと。次にコ ンタクトレンズを着用していて容易に外せる場合は外す こと。その後も洗浄を続けること。 |
|
ジアクリル酸無水物 価格
もっと(9)
メーカー |
製品番号 |
製品説明 |
CAS番号 |
包装 |
価格 |
更新時間 |
購入 |
富士フイルム和光純薬株式会社(wako)
|
W01COBQH-7998 |
アクリル酸無水物
Acrylic anhydride |
2051-76-5 |
5g |
¥10000 |
2024-03-01 |
購入 |
富士フイルム和光純薬株式会社(wako)
|
W01COBQH-7998 |
Acrylic anhydride |
2051-76-5 |
25g |
¥14000 |
2024-03-01 |
購入 |
富士フイルム和光純薬株式会社(wako)
|
W01COBQH-7998 |
Acrylic anhydride |
2051-76-5 |
25g×4 |
¥157500 |
2024-03-01 |
購入 |
富士フイルム和光純薬株式会社(wako)
|
W01COBQH-7998 |
アクリル酸無水物
Acrylic anhydride |
2051-76-5 |
1g |
¥10000 |
2023-06-01 |
購入 |
富士フイルム和光純薬株式会社(wako)
|
W01COBQH-7998 |
Acrylic anhydride |
2051-76-5 |
10g |
¥31500 |
2023-06-01 |
購入 |
ジアクリル酸無水物 化学特性,用途語,生産方法
外観
無色~ほとんど無色透明液体
使用
Acrylic anhydride can be used to prepare specialty acrylate, acrylamide monomers or acrylic resin. It forms cyclic anhydrides on polymerization and can not be used as a crosslinker.
合成
The synthesis of Acrylic anhydride is as follows:
In a 3-liter, four-necked glass reactor provided with a thermometer and a stirrer were placed, in a dry air atmosphere, 1,240 g of methylene chloride, 1.08 g (0.5% by mass) of Sumilizer GM, 0.65 g (0.3% by mass) of Sumilizer TP-D, 0.65 g (0.3% by mass) of Sumilizer WX-R, 216 g (3.0 mol) of acrylic acid and 264 g (1.5 mol) of benzenesulfonyl chloride. The mixture was cooled to 5°C. Then, 304 g (3.0 mol, 1 equivalent relative to the acids generated from benzenesulfonyl chloride) of triethylamine was dropwise added in 2 hours with the temperature of the reaction mixture being controlled at 30°C or lower. After the completion of the dropwise addition, stirring was made for 1 hour with the same temperature being kept. The reaction mixture was analyzed by GC, which indicated that the conversion of acrylic acid was 99%. After the completion of the reaction, 375 g of water was added to the reaction mixture to wash the reaction mixture. The reaction mixture was further washed twice each time with 563 g of water, after which distillation was conducted to remove methylene chloride. The yield of the acrylic acid anhydride obtained was 172 g and 91% and its purity by GC analysis was 99%, and no high-molecular by-product was detected.
ジアクリル酸無水物 上流と下流の製品情報
原材料
準備製品
ジアクリル酸無水物 生産企業
Global( 186)Suppliers
ジアクリル酸無水物 スペクトルデータ(1HNMR)
2051-76-5(ジアクリル酸無水物)キーワード:
- 2051-76-5
- ACRYLIC ANHYDRIDE
- 2-PROPENOIC ACID ANHYDRIDE
- Acyrlic acid anhydride
- PROPENOIC ANHYDRIDE
- Diacrylic anhydride
- acrylic acid acryloyl ester
- 2-Propenoic acid,1,1'-anhydride
- ACRYLIC ANHYDRIDE (STABL. WITH 10% 4-METHOXYPHENOL)
- JACS-2051-76-5
- Acrylic Anhydride (stabilized with MEHQ)
- ACRYLIC ACID ANHYDRIDE
- prop-2-enoyl prop-2-enoate
- Acrylic anhydride (6CI, 7CI, 8CI)
- ビスアクリル酸無水物
- 無水アクリル酸
- ジアクリル酸無水物
- アクリル酸無水物
- アクリル酸無水物 (stabilised with 10% 4-Methoxyphenol)
- ビスプロペン酸1,1′-無水物
- プロパ-2-エノイル プロパ-2-エノアート