トリフルオロチタン(III)
トリフルオロチタン(III) 物理性質
- 融点 :
- 1200 °C
- 沸点 :
- 1400 °C
- 比重(密度) :
- 3.4 g/mL at 25 °C(lit.)
- 溶解性:
- insoluble in H2O, dilute acid solutions, alkaline solutions
- 外見 :
- 結晶性粉末
- 比重:
- 3.4
- 色:
- 赤から茶色
- 水溶解度 :
- 難溶性。水中で加水分解します。
- Sensitive :
- Air & Moisture Sensitive
- Crystal Structure:
- VF3型
- 晶系:
- 三方
- 空间群:
- R3c
- 晶格常数:
| a/nm | b/nm | c/nm | α/o | β/o | γ/o | V/nm3 |
| 0.543 | 0.543 | 1.364 | 90 | 90 | 120 | 0.3488 |
- 暴露限界値:
- ACGIH: TWA 2.5 mg/m3
NIOSH: IDLH 250 mg/m3; TWA 2.5 mg/m3
- CAS データベース:
- 13470-08-1(CAS DataBase Reference)
- EPAの化学物質情報:
- Titanium fluoride (TiF3) (13470-08-1)
安全性情報
- リスクと安全性に関する声明
- 危険有害性情報のコード(GHS)
| 絵表示（GHS） |
|
| 注意喚起語 |
危険 |
| 危険有害性情報 |
| コード |
危険有害性情報 |
危険有害性クラス |
区分 |
注意喚起語 |
シンボル |
P コード |
| H314 |
重篤な皮膚の薬傷?眼の損傷 |
皮膚腐食性/刺激性 |
1A, B, C |
危険 |
|
P260,P264, P280, P301+P330+ P331,P303+P361+P353, P363, P304+P340,P310, P321, P305+ P351+P338, P405,P501 |
|
| 注意書き |
| P260 |
粉じん/煙/ガス/ミスト/蒸気/スプレーを吸入しないこ と。 |
| P280 |
保護手袋/保護衣/保護眼鏡/保護面を着用するこ と。 |
| P303+P361+P353 |
皮膚（または髪）に付着した場合：直ちに汚染された衣 類をすべて脱ぐこと/取り除くこと。皮膚を流水/シャワー で洗うこと。 |
| P305+P351+P338 |
眼に入った場合：水で数分間注意深く洗うこと。次にコ ンタクトレンズを着用していて容易に外せる場合は外す こと。その後も洗浄を続けること。 |
| P363 |
汚染された衣類を再使用す場合には洗濯をすること。 |
|
トリフルオロチタン(III) 価格
もっと(7)
| メーカー |
製品番号 |
製品説明 |
CAS番号 |
包装 |
価格 |
更新時間 |
購入 |
|
富士フイルム和光純薬株式会社(wako)
|
W01ALF013079 |
ふっ化チタン(III)
Titanium(III) fluoride |
13470-08-1 |
10g |
￥28400 |
2024-03-01 |
購入 |
|
富士フイルム和光純薬株式会社(wako)
|
W01ALF013079 |
ふっ化チタン(III)
Titanium(III) fluoride |
13470-08-1 |
50g |
￥120800 |
2024-03-01 |
購入 |
|
Sigma-Aldrich Japan
|
399817 |
フッ化チタン(III)
Titanium(III) fluoride |
13470-08-1 |
5g |
￥6320 |
2024-03-01 |
購入 |
|
富士フイルム和光純薬株式会社(wako)
|
W01SRM93-2224 |
ふっ化チタン(III), min. 98%
Titanium(III) fluoride, min. 98% |
13470-08-1 |
5g |
￥17600 |
2024-03-01 |
購入 |
|
富士フイルム和光純薬株式会社(wako)
|
W01SRM93-2224 |
ふっ化チタン(III), min. 98%
Titanium(III) fluoride, min. 98% |
13470-08-1 |
25g |
￥64100 |
2024-03-01 |
購入 |
トリフルオロチタン(III) 化学特性,用途語,生産方法
化学的特性
Red to brown crystalline powder
Blue rhombic crystals are stable in air and unusually resistant to acids and bases. Sublimation begins at about 930°C in a less than 0.1 mm vacuum. M.p. >1100°C; d%5 2.98. Insoluble in water and alcohol. Disproportionation to TiF4 and Ti begins at 950°C.
使用
It is used as a laboratory chemicals & for manufacture of chemicals.
調製方法
Titanium metal is hydrogenated at 600-700°C. It is then placed in a small nickel boat and inserted into the horizontal nickel tube (closed at one end). The hydride is fluorinated with gaseous HF. The open end of the tube has a cooling jacket and is sealed with picein to a copper cover. Two copper tubes are silver-soldered into the cover and serve as an inlet and outlet for the hydrogen; the inlet tube also contains a concentric silver tube for introducing HF. The output gases pass through an empty polyethylene bottle, a bubble counter filled with paraffin oil and a polyethylene trap to freeze excess HF gas. The closed end of the reaction tube is placed in a tubular furnace. The temperature is measured externally. After thoroughly flushing the apparatus with Hs, fluorination followed with a 1 4 mixture of H2 and HF for four to five hours. The HF flow is first started at a temperature above 200°C. The water temperature in the cooling jacket should be higher than 20°C to prevent condensation of the HF. After completion of the fluorination, the product is left to cool in a stream of hydrogen. The yield is 90%.
参考文献
R. Hoppe, S. Becker, Z. Anorg. Allg. Chem., 568, 126 (1989).
トリフルオロチタン(III) 上流と下流の製品情報
原材料
準備製品
トリフルオロチタン(III) 生産企業
Global( 81)Suppliers
13470-08-1(トリフルオロチタン(III))キーワード:
- 13470-08-1
- TiF3
- Titanium fluoride (TiF3)
- titaniumfluoride(tif3)
- TITANIUM TRIFLUORIDE
- TITANIUM(III) FLUORIDE
- TITANIUM FLUORIDE
- Titanium(III)fluoride99%
- Titanium(III) fluoride, min. 98%
- Titanium(III) trifluoride
- TSCS(13470-08-1)
- Titanium(III)fluoride,min.98%
- Titanium(III) fluoride,98%
- Titanium fluoride(F3Ti)
- itanium(III)fluoride
- Carbon Graphite (C) Sputtering Targets
- ふっ化チタン(III)
- 三ふっ化チタン
- トリフルオロチタン(III)
- チタン(III)トリフルオリド
- ふっ化チタン(III), min. 98%
- トリフルオロチタン