PFA-14
| 中文名称 | PFA-14 |
|---|---|
| 中文同义词 | 聚氟烷氧基微粉;纳米PFA微粉;PFA粉;可熔融PTFE微粉;PFA树脂;高品质 PFA微粉 |
| 英文名称 | 3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,11,11,12,12,13,13,14,14,15,15,16,16,16-nonacosafluorohexadecanol |
| 英文同义词 | 3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,11,11,12,12,13,13,14,14,15,15,16,16,16-nonacosafluorohexadecanol;1-Hexadecanol, 3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,11,11,12,12,13,13,14,14,15,15,16,16,16-nonacosafluoro-;3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,11,11,12,12,13,13,14,14,15,15,16,16,16-Nonacosafluoro-1-hexadecanol;1,1,2,2-Tetrahydroperfluoro-1-hexadecanol;Einecs 262-382-7;PFA-14;Polyfluoroalkoxy micropowder;PFA micropowder |
| CAS号 | 60699-51-6 |
| 分子式 | C16H5F29O |
| 分子量 | 764.16 |
| EINECS号 | 262-382-7 |
| 相关类别 | Organics |
| Mol文件 | 60699-51-6.mol |
| 结构式 |  |
PFA-14 性质
| 沸点 | 284.8±40.0 °C(Predicted) |
|---|---|
| 密度 | 1.702±0.06 g/cm3(Predicted) |
| 酸度系数(pKa) | 14.28±0.10(Predicted) |
| EPA化学物质信息 | 1-Hexadecanol, 3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,11,11,12,12,13,13,14,14,15,15,16,16,16-nonacosafluoro- (60699-51-6) |
PFA的英文名称为：Polyfluoroalkoxy，中文名称为：四氟乙烯—全氟烷氧基乙烯基醚共聚物 (又称：过氟烷基化物，可溶性聚四氟乙烯) 。PFA树脂相对来说是比较新的可熔融加工的氟塑料，PFA 、FEP、PTFE 的化学性能相似，但FEP只能在200度以下使用，PTFE不能注塑。PFA是TFE与少量全氟烷基乙烯基醚（通常是全氟正丙基乙烯基醚，简称PPVE）的共聚物，相当于PTFE分子主链上的氟原子被全氟烷氧基取代后的产物PFA粉除了可以采用挤出和模压工艺外，还可以采用注射、传递模、滚塑、浸涂、喷涂等加工工艺，可以制成线缆、管、片、膜、涂层及其他复杂形状的制品，用途几乎涵盖PTFE所涉领域。
PFA可通过TFE和PPVE的自由基聚合反应得到，高压釜内加原料、水、分散剂、引发剂等进行共聚，经分离后可得粗PFA细粉。PFA生产过程中的主要技术壁垒在于PPVE制备，反应原理大致为HFP氧化得HFPO，HFPO在催化剂作用下异构化成中间体全氟丙酰氟，全氟丙酰氟再与HFPO加成即得全氟烷氧基酰氟，之后再与硫酸钾或碳酸钠一起在250～300℃进行脱羧反应即得PPVE。
另外，PFA在聚合过程中会因引发剂产生热不稳定端基，影响产品质量，需采用湿热处理以及元素氟氟化将不稳定端基转化成稳定的全氟基团。