ホウ化カルシウム（６：１） 化学特性,用途語,生産方法
説明
Typical samples of CaB
6 are nonstoichiometric, i.e. the
ratio of boron to calcium is not exactly 6:1, for example
the ultra-fine powders of CaB
6 produced by some
researchers had B:Ca ratio of 5.91:1. It is an important
material due to its high electrical conductivity, hardness,
chemical stability, and melting point.
化学的特性
black cub; -200 mesh 99.5% pure; refractory material [KIR78] [CER91] [CRC10]
物理的性質
Calcium boride is a black,
lustrous, chemically inert powder with a low density.
Calcium hexaboride is insoluble in H
2O, MeOH (methanol),
and EtOH (ethanol) and dissolves slowly in acids.
It has the cubic structure typical for metal hexaborides,
with octahedral units of six boron atoms combined
with calcium atoms.
使用
Calcium boride is used as an electrode (cathode) material and n-type thermoelectric materials. It is used to make boron- alloyed steel, as a deoxidation agent in the production of oxygen-free copper. It is further used as an antioxidant in carbon bonded refractories. It acts as a new material which is used in the nuclear-industry for neutron- preventing, high-purity metal borid (TiB2,ZrB2,HfB2) and high-purity boron alloy(Ni-B, Co-B, Cu-b).
製造方法
Calcium boride can be formed directly from the
elements. Ca melts at 842°C and boron melts at
2076°C. Therefore, if a vapor of Ca metal at >850°C
(red-heat) is passed over crystals of boron, a gas–solid
reaction forms the desired boride. However, to obtain
stoichiometric compositions, it is better to heat the
well-mixed powders of Ca and B to obtain specific
compounds:
Ca+ 6B→CaB
6